Titanium Grade 2 are unalloyed and generally known as CP (Commercially Pure). The tensile and yield strength of titanium generally increases with the grade number. Titanium is 30% stronger than Steel but nearly 50% lighter and although Aluminium is lighter, Titanium is stronger and has excellent strength retention. Due to Titanium's weight, strength and high corrosion resistance it is very popular in various manufacturing industries from aerospace, medical, shipping, military etc.
Chemical Composition Limits | ||||||
Weight % | Ti | C | Fe | N | O | H |
Titanium CP Grade 2 | bal | 0.08 | 0.30 | 0.05 | 0.020 | 0.015 |
Material | Tensile Strength min | Yield Strength | Elongation (%) | ||
ksi | Mpa | ksi | MPa | ||
Titanium CP Grade 2 Annealed Sheet |
50 | 345 | 40-65 | 276-448 | 20 |
Product Details:
Size/Diameter | 1 inch |
Diameter | 2 inches |
Shape | Square |
Single Piece Length | 6 meter |
Usage/Application | Manufacturing |
Country of Origin | Made in India |
Titanium Grade 5 is the most commonly used alloy. Ti6Al4V is significantly stronger than other commercially pure titanium whilst still retaining the same stiffness and thermal properties (excluding thermal conductivity). Titanium Grade 5 extensively used in Aerospace, Medical, Marine and Chemical Processing.
Chemical Composition Limits | ||||||||||
Weight % | Ti | C | Fe | N | Al | O | V | H | Y | Other |
Ti-6Al-4V | bal | 0.08 | 0.03 | 0.05 | 5.5-6.75 | 0.20 | 3.5-4.5 | 0.015 | 0.005 | 0.40 |
Material | Diameter | Tensile Strength min | Yield Strength | Elongation in 2" | Reduction of Area % | ||
ksi | Mpa | ksi | MPa | ||||
Titanium Alpha-Beta Ti-6Al-4V Annealed Bar (min) |
<2.00" | 135 | 931 | 125 | 862 | 10 | 25 |
Titanium Alpha-Beta Ti-6Al-4V Annealed Bar (min) |
2.00" - 4.00" | 130 | 896 | 120 | 827 | 10 | 25 |
Titanium Alpha-Beta Ti-6Al-4V Annealed Bar (min) |
>4.00" | 130 | 896 | 120 | 827 | 8 | 20 |